Review of Multiaxial Testing for Very High Cycle Fatigue: From ‘Conventional’ To Ultrasonic Machines.

Costa, P., Nwawe, R., Soares, H., Reis, L., Freitas, M. and Montalvão, D., 2020. Review of Multiaxial Testing for Very High Cycle Fatigue: From ‘Conventional’ To Ultrasonic Machines. Machines, 8 (2), 25.

Full text available as:

[img]
Preview
PDF (V2 of OPEN ACCESS ARTICLE)
machines-08-00025-v2.pdf - Published Version
Available under License Creative Commons Attribution.

10MB
[img]
Preview
PDF (Open Access article)
machines-08-00025.pdf - Published Version
Available under License Creative Commons Attribution.

3MB

Official URL: https://www.mdpi.com/2075-1702/8/2/25

Abstract

Fatigue is one of the main causes for in service failure of mechanical components and structures. With the development of new materials, such as high strength aluminium or titanium alloys with different microstructures from steels, materials no longer have a fatigue limit in the classical sense, where it was accepted that they would have ‘infinite life’ from 10 million (107) cycles. The emergence of new materials used in critical mechanical parts, including parts obtained from metal additive manufacturing (AM), the need for weight reduction and the ambition to travel greater distances in shorter periods of time, have brought many challenges to design engineers, since they demand predictability of material properties and that they are readily available. Most fatigue testing today still uses uniaxial loads. However, it is generally recognised that multiaxial stresses occur in many full-scale structures, being rare the occurrence of pure uniaxial stress states. By combining both Ultrasonic Fatigue Testing with multiaxial testing through Single-Input-Multiple-Output Modal Analysis, the high costs of both equipment and time to conduct experiments have seen a massive improvement. It is nowadays possible to test materials under multiaxial loading conditions and for very high number of cycles in a fraction of the time compared to non-ultrasonic fatigue testing methods (days compared to months or years). This work presents the current status of ultrasonic fatigue testing machines working at a frequency of 20 kHz to date, with emphasis on multiaxial fatigue and very high cycle fatigue. Special attention will be put into the performance of multiaxial fatigue tests of classical cylindrical specimens under tension/torsion and flat cruciform specimens under in-plane bi-axial testing using low cost piezoelectric transducers. Together with the description of the testing machines and associated instrumentation, some experimental results of fatigue tests are presented in order to demonstrate how ultrasonic fatigue testing can be used to determine the behaviour of a steel alloy from a railway wheel at very high cycle fatigue regime when subjected to multiaxial tension/torsion loadings.

Item Type:Article
ISSN:2075-1702
Uncontrolled Keywords:piezoelectric machine; ultrasonic fatigue testing (UFT); biaxial fatigue; cruciform specimens; very high cycle fatigue (VHCF); multiaxial loading
Group:Faculty of Science & Technology
ID Code:33995
Deposited By: Unnamed user with email symplectic@symplectic
Deposited On:12 May 2020 15:29
Last Modified:01 Jun 2020 15:23

Downloads

Downloads per month over past year

More statistics for this item...
Repository Staff Only -