Chen, L., Wang, Z., Zhu, H., Burr, P. A., Qu, J., Huang, Y., Balogh, L., Preuss, M. and Muránsky, O., 2022. On the Microstructure and High-Temperature Stability of Nano-Grained Zircaloy-4. Scripta Materialia, 210 (March), 114410.
Full text available as:
|
PDF
SMM-S-21-02281 accepted.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. 1MB | |
Copyright to original material in this document is with the original owner(s). Access to this content through BURO is granted on condition that you use it only for research, scholarly or other non-commercial purposes. If you wish to use it for any other purposes, you must contact BU via BURO@bournemouth.ac.uk. Any third party copyright material in this document remains the property of its respective owner(s). BU grants no licence for further use of that third party material. |
DOI: 10.1016/j.scriptamat.2021.114410
Abstract
A nano-grained microstructure of an α-Zr alloy (Zircaloy-4) was produced by high-pressure torsion, which shows evidence of a metastable ω-Zr phase, rather than β-Zr, determined by combining synchrotron X-ray diffraction and detailed electron microscopy observations. The ω-Zr phase is retained at ambient conditions and shows a new orientation relationship of [-1011] α // [-1100] ω and (-101-1) α // (-1-120) ω with the α-Zr matrix but is thermally unstable, fully reverting back to α-Zr phase upon heating above 350 °C.
Item Type: | Article |
---|---|
ISSN: | 1359-6462 |
Uncontrolled Keywords: | Zirconium alloys; High-pressure torsion; Microstructure; Stability |
Group: | Faculty of Science & Technology |
ID Code: | 36206 |
Deposited By: | Symplectic RT2 |
Deposited On: | 06 Nov 2021 11:09 |
Last Modified: | 21 Nov 2022 01:08 |
Downloads
Downloads per month over past year
Repository Staff Only - |