Levenets, A.V., Rusakova, H.V., Fomenko, L.S., Huang, Y., Kolodiy, I.V., Vasilenko, R.L., Tabachnikova, E.D., Tikhonovsky, M.A. and Langdon, T.G., 2022. Structure and low temperature micromechanical properties of as-cast and SPD-processed high-entropy Co25-xCr25Fe25Ni25Cx alloys. Low Temperature Physics, 48 (7), 560.
Full text available as:
|
PDF
Elena-paper_final.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial. 1MB | |
Copyright to original material in this document is with the original owner(s). Access to this content through BURO is granted on condition that you use it only for research, scholarly or other non-commercial purposes. If you wish to use it for any other purposes, you must contact BU via BURO@bournemouth.ac.uk. Any third party copyright material in this document remains the property of its respective owner(s). BU grants no licence for further use of that third party material. |
DOI: 10.1063/10.0011605
Abstract
The effect of carbon additions on the structure and mechanical properties of high-entropy alloys Co25-xCr25Fe25Ni25Cx (x = 0, 1, 3, at. %) in two structural states, as-cast coarse-grained (CG) samples and nanocrystalline (NC) obtained by severe plastic deformation (SPD), was studied. The SPD was performed by high-pressure torsion at room temperature. The mechanical properties were investigated by microindentation in the temperature range of T = 77-300 K. It was found that in the as-cast state, all alloys had a dendritic microstructure and an inhomogeneous distribution of elements. At x = 0 and x = 1, the dendrites were enriched in iron and nickel, and the interdendrite regions were enriched in chromium. At x = 3, in the interdendrite regions, a eutectic consisting of a multicomponent matrix and fine eutectic dendrites of M7C3 carbide, where M is predominantly chromium, was formed. The main phase in alloys had an fcc lattice, while the solubility of carbon in it was about 1 at. %. SPD led to effective refinement of the microstructure (the size of the coherent scattering regions was about 30-50 nm), to an increase in the dislocation density up to (1-1.5)×1015 m-2 and to an increase in the concentration of stacking faults. The microhardness of CG alloys at room temperature increased monotonically with increasing carbon concentration, while in NC alloys the maximum microhardness HV was achieved at 1 at. % of carbon. The reason for this anomalous behavior of the microhardness of NC alloys is an increase in the grain size and a decrease in the dislocation density in the alloy with x = 3 compared to the alloy with x = 1. As the temperature decreased from room temperature to the temperature of liquid nitrogen, the microhardness of CG and NC alloys increased by about 1.5-1.7 and 1.2-1.5 times, respectively, which indicates the thermallyactivated nature of plastic deformation under the indenter. The results obtained indicate that the main role in the hardening of the CG alloys Co25-xCr25Fe25Ni25Cx is due to solid solution and dispersion hardening, while in NC alloys it is hardening due to a decrease in the grain size (according to the Hall-Petch relation) and an increase in the dislocation density (according to the Taylor relation).
Item Type: | Article |
---|---|
ISSN: | 0132-6414 |
Additional Information: | A.L. and M.T. were supported by the National Research Foundation of Ukraine in frame of the project No. 2020.02/0327 (Fundamental aspects of the new materials creation with unique physical, mechanical and radiation properties based on the concentrated multicomponent alloys). T.G.L. and Y.H. were supported by the European Research Council under Grant Agreement No. 267464-SPDMETALS |
Uncontrolled Keywords: | high-entropy alloys, carbon alloying, microstructure, microhardness, severe plastic deformation, deformation mechanisms |
Group: | Faculty of Science & Technology |
ID Code: | 36861 |
Deposited By: | Symplectic RT2 |
Deposited On: | 25 Apr 2022 08:33 |
Last Modified: | 19 Jul 2022 13:14 |
Downloads
Downloads per month over past year
Repository Staff Only - |