Hanna, A., Azzeddine, H., Avettand-Fènoël, M-N., Baudin, T., Huang, Y. and Langdon, T. G., 2024. DSC analysis of dissolution reaction in an as-cast and HPT-processed Mg-Gd alloy. Materials Letters, 376, 137293.
Full text available as:
PDF
Hiba-MaterChar_revised.pdf - Accepted Version Restricted to Repository staff only until 5 September 2025. Available under License Creative Commons Attribution Non-commercial No Derivatives. 564kB | |
Copyright to original material in this document is with the original owner(s). Access to this content through BURO is granted on condition that you use it only for research, scholarly or other non-commercial purposes. If you wish to use it for any other purposes, you must contact BU via BURO@bournemouth.ac.uk. Any third party copyright material in this document remains the property of its respective owner(s). BU grants no licence for further use of that third party material. |
DOI: 10.1016/j.matlet.2024.137293
Abstract
The dissolution reaction kinetics were determined by differential scanning calorimetry (DSC) analysis for Mg-0.6Gd (wt.%) in an as-cast condition and after processing by high-pressure torsion (HPT) at room temperature for 20 turns. For the as-cast condition, the dissolution temperature was in the range of 634–658 K with an activation energy of 135±9 kJ/mol. After HPT, the range of dissolution temperature decreased to 601–633 K, with a lower activation energy of 118±10 kJ/mol. In both conditions, the Avrami and growth exponents are around 1.5, which suggests that the dissolved precipitates exhibit polyhedron-like morphology and that the dissolution process is dominated by bulk dissolution with a constant rate controlled by diffusion.
Item Type: | Article |
---|---|
ISSN: | 0167-577X |
Group: | Faculty of Science & Technology |
ID Code: | 40267 |
Deposited By: | Symplectic RT2 |
Deposited On: | 30 Aug 2024 11:00 |
Last Modified: | 12 Sep 2024 07:23 |
Downloads
Downloads per month over past year
Repository Staff Only - |