Gonzalez, R., Hernandez Battez, A., Viesca, J.L., Higuera-Garrido, A. and Fernandez-Gonzalez, A., 2013. Lubrication of DLC Coatings with Two Tris(pentafluoroethyl)trifluorophosphate Anion-Based Ionic Liquids. Tribology Transactions, 56 (5), 887 - 895 .
Full text available as:
Paper.pdf - Accepted Version
The lubrication of a Cr-DLC coating with ethyl-dimethyl-2-methoxyethylammonium tris(pentafluoroethyl)trifluoropho-sphate [(NEMM)MOE][FAP] and 1-butyl-1-methylpyrro-lidinium tris(pentafluoroethyl)trifluorophosphate [BMP] [FAP] ionic liquids (ILs) as 1 wt% additives to a polyalphaolefin (PAO 6) was studied. Zinc dialkyldithiophosphate (ZDDP) was also used as reference in order to evaluate the effectiveness of the ILs. Reciprocating ball-on-plate tribological tests at loads of 20 and 40 N were performed. The results showed that both ILs exhibited a friction reduction, especially at the lowest load tested. Antiwear properties were also improved; the PAO 6 + 1% [BMP][FAP] mixture was slightly better, close to the values for PAO 6 + 1% ZDDP. Scanning electron microscopy (SEM) images and X-ray photoelectron spectroscopy (XPS) analysis indicated that the additive–surface interaction was responsible for the tribological improvement.
|Additional Information:||Published 06 Aug 2013. Twelve month embargo on author final version.|
|Group:||Faculty of Science and Technology|
|Deposited By:||Unnamed user with email symplectic@symplectic|
|Deposited On:||24 Feb 2014 12:16|
|Last Modified:||10 Sep 2014 14:57|